Toyo International - Malaysia largest custom and private label grease & Lubricant manufacturer
 
 
 
 
 
 
  Grease Ready Reference
 
 Abbreviations  Definition of Terms Relating To Lubricating Grease
 
 

ASTM
American Society for Testing and Materials

ISO
International Standards Associations

FDA
Food and Drug Administration

JIS
Japan Industry Standard

NLGI
National Lubricating Grease Institute

OEM
Original Equipment Manufacturer
SAE
Society of Automotive Engineers
AGMA
American Gear Manufacturers Association
Source : NTN BEARING CORPORATION
Compiled by : Angie Ng, TOYO GREASE MANUFACTURING (M) SDN BHD
 
Relubrication Guidelines
It cannot be stated strongly enough that when relubricating a bearing unit it is essential to choose a clean lubricant compatible with the grease already in the bearing.

Whether or not different kinds of grease may be mixed depends on the thickening agents used in making the grease. Mixing different types of grease can affect key properties and alter the grease’s performance. If these key properties are diminished, the grease can become ineffective, leading to premature bearing failure. (Refer to Table 1 for further information.)
Pump the grease gun once prior to connecting it to the fitting to purge the nozzle of any contaminants that may have accumulated and wipe it with a clean towel. The grease fitting also merits inspection for contaminants and should also be wiped clean.

Taking these precautionary measures to prevent the introduction of contaminants into the bearing will help ensure the proper operation of the bearing and performance to and beyond the rated life of the bearing.

Table 1: Grease thickener compatibility
   
 
Aluminum Complex
Barium
Calcium
Calcium
12- Hydroxy
Calcium Complex
Clay
Lithium
Lithium
12-hydroxy
Lithium Complex
Polyurea
Aluminum Complex
Barium
Calcium
Calcium 12- Hydroxy
Calcium Complex
Clay
Lithium
Lithium 12-hydroxy
Lithium Complex
Polyurea

Table key
Circle: Mixing greases will not produce any appreciable change in properties
Square: Mixing greases may produce considerable variation in properties
Triangle: Mixing greases will cause drastic changes in properties

As for the quantity of lubricant used, most applications require only two pumps of grease. This is an instance where more is not better. Over packing the bearings during relubrication should be avoided. Too much grease may create a "churning" action within the bearing, which in turn results in the bearing running hotter. This leads to premature deterioration of the grease and ultimately bearing failure.


ROLLING ELEMENT BEARINGS FAILURE INVESTIGATION
Rolling element bearings may fail for many reasons. Research by expert engineers have determine the cause of failures through experiential tests and have been carefully documented.
The data base documents failures of rolling element includes :

l FATIGUE FLAKE
l CORROSION
l FALSE BRINELLING
l OUTER RACE FRETTING
l INNER RACE SPINNING
l UNEVEN FATIGUE
l ROLLER END COLLAPSE
l ROLLER PEELING
l UNEVEN WEAR MARKS
l ROLLER END CHIPPING
l ROLLER BREAKAGE

l MAGNETIC DAMAGE
l GREASE FAILURE
l OVERHEATING
l ABRASION
l ROLLER STAINING
l BRINELLING
l FRACTURED FLANGE
l INNER RACE FRETTING
l SKEW RUNNING MARKS
l LADDER MARKING
l MOLTEN CAGE
l SMEARING

When machines experience a failure, your first approach is to collect technical information and failure history.
Take an OVERVIEW rather than the NARROWER approach of investigating the apparent immediate problem and carry out a macro-analysis.
 
 
 
 
 
 